Author Topic: PK freshly anodised # NEW PICS ADDED Pg1 #  (Read 3002 times)

0 Members and 1 Guest are viewing this topic.

Offline MartyC

  • Berm Worm
  • ***********
  • Posts: 8755
  • Radder than a Rad thing on a Rad day; maybe?
  • Rated:
Re: PK freshly anodised!
« Reply #25 on: November 13, 2007, 11:00 PM »
That's looking very cool  :coolsmiley:


Better to crash and burn than fade away

darkersomeday

  • Guest
Re: PK freshly anodised!
« Reply #26 on: November 13, 2007, 11:11 PM »
that actually looks really cool :daumenhoch:

big pimpin :shocked:

looking forward to seeing this built :knuppel2:

darkslider

  • Guest
Re: PK freshly anodised!
« Reply #27 on: November 13, 2007, 11:23 PM »
Very tasty work. Reckon he could fettle this up? I'm worried about the two tone effect! Like the Selector, and Madness though!

SaMAlex

  • Guest
Re: PK freshly anodised!
« Reply #28 on: November 13, 2007, 11:27 PM »
Its hard to re-anodise stems cos of the steel shaft: it will desolve in the anodising process. If the shaft comes away from the ally body (like a pro/tuff neck) then its do-able, but the fit might not be as good cos the process will change the hole size a little as it removes a tiny bit of material from the ally.

darkslider

  • Guest
Re: PK freshly anodised!
« Reply #29 on: November 13, 2007, 11:44 PM »
Apparently the brute wedge doesn't remove! See Redline Proline II thread! Cheers Alex :daumenhoch:

customparts

  • Guest
Re: PK freshly anodised!
« Reply #30 on: November 14, 2007, 10:08 AM »
the steel bar can be masked off with this tape we have got,  its acid proof so as long as the ali is anodisable then its ok with the bar in :daumenhoch:
CCA

Offline generallee

  • Look Back
  • *****
  • Posts: 1539
  • Rated:
Re: PK freshly anodised!
« Reply #31 on: November 14, 2007, 12:34 PM »
new pics added to to the top of this thread!

Frosty

  • Guest
Re: PK freshly anodised!
« Reply #32 on: November 14, 2007, 12:37 PM »
What about inside the stem steel shaft, or are the parts not submerged in acid??

teamsano

  • Guest
Re: PK freshly anodised!
« Reply #33 on: November 15, 2007, 09:49 PM »
the steel bar can be masked off with this tape we have got,  its acid proof so as long as the ali is anodisable then its ok with the bar in :daumenhoch:
CCA

that sounds like flannel.

frame looks nice, purple is a bit mtb tho.

Donker

  • Guest
Re: PK freshly anodised!
« Reply #34 on: November 23, 2007, 03:28 PM »
the steel bar can be masked off with this tape we have got,  its acid proof so as long as the ali is anodisable then its ok with the bar in :daumenhoch:
CCA

that sounds like flannel.

frame looks nice, purple is a bit mtb tho.

it isnt flannel, it can be done. :Great_Britain:

pic1london

  • Guest
Re: PK freshly anodised # NEW PICS ADDED Pg1 #
« Reply #35 on: November 25, 2007, 12:57 AM »
Nice job there Steve...
Very good price too.
 
The quote I gave you a while back was for all the polishing & a 3 week turnaround door to door. Taking it there & back by hand no postage.... Just thought I needed to clear that up.

Re; the tape/redline stem question?

Yes it can be done.
Lead tape (for roofing) is the trick...Approx £100 a roll.
Plus you have to plug up the holes..



RADBMX.CO.UK  |  Technical & Reference Section  |  Tech and Restoration  |  PK freshly anodised # NEW PICS ADDED Pg1 #
 

gfxgfx
gfx gfx
Powered by MySQL Powered by PHP Valid XHTML 1.0! Valid CSS!
SimplePortal 2.3.5 © 2008-2012, SimplePortal